Failure Analysis of the M16 Rifle Bolt
V.Y. Yu*, J.G. Kohl, R.A. Crapanzano, M.W. Davies, A.G. Elam, M.K. Veach
Department of Civil and Mechanical Engineering
United States Military Academy
West Point, NY 10996, USA
4. Conclusions
The fracture of the M16 bolt resulted from a cumulative effect of high stress concentrations at the fillet radius and the additional stress concentration imposed by the presence of localized pitting at the surface. The bolt possesses many fillet regions which impose numerous areas of high stress concentration. In particular, two fillets experienced higher stress immediately adjacent to the round extractor due to the non-contiguous feature of the bolt. These two specific areas of high stress concentration also corresponded to the same location where failure of the bolt occurred in all fractured bolt specimens. Micrographs obtained from the scanning electron microscope of the fractured surface showed localized pitting at the failure initiation site. In addition, transgranular crack propagation near the pit formations in the fillet regions was observed. The localized pits formed near the locking lugs also served as high stress concentration points. The presence of pits in the material amplified the stresses of the bolt in the locking lug region which already had a high stress concentration due to the irregular geometry of the bolt. This cumulative stress concentration provides a good indicator why the crack initiated and propagated from this region.
The wear observed in the controlled experiment indicates the mechanism of why the corrosion pits formed near the locking lug fillet by exposing the Carpenter Steel 158 base metal to the environment. Vickers microhardness readings near the fillet region show that the bolt was not uniformly case hardened. Comparison of the microhardness readings near the fillet region and 10 mm from this region show a disparity of approximately 100 units. The softer, less carburized region near the fillet contributes to the formation of a wear area after firing just 1800 rounds.
"What would a $2,000 Geissele Super Duty do that a $500 PSA door buster on Black Friday couldn't do?" - Stopsign32v
Bookmarks